Hydroxyl-terminated P(S-r-MMA) random copolymers (RCPs) with molecular weights (Mn) from 1700 to 69000 and a styrene unit fraction of approximately 61% were grafted onto a silicon oxide surface and subsequently used to study the orientation of nanodomains with respect to the substrate, in cylinder-forming PS-b-PMMA block copolymer (BCP) thin films. When the thickness (H) of the grafted layer is greater than 5–6 nm, a perpendicular orientation is always observed because of the efficient decoupling of the BCP film from the polar SiO2 surface. Conversely, if H is less than 5 nm, the critical thickness of the grafted layer, which allows the neutralization of the substrate and promotion of the perpendicular orientation of the nanodomains in the BCP film, is found to depend on the Mn of the RCP. In particular, when Mn = 1700, a 2.0 nm thick grafted layer is sufficient to promote the perpendicular orientation of the …
Publisher: 
American Chemical Society
Publication date: 
15 May 2015
Authors: 

Katia Sparnacci, Diego Antonioli, Valentina Gianotti, Michele Laus, Federico Ferrarese Lupi, Tommaso Jacopo Giammaria, Gabriele Seguini, Michele Perego

Biblio References: 
Volume: 7 Issue: 20 Pages: 10944-10951
Origin: 
ACS applied materials & interfaces