Chemically L10 ordered (001) textured FePt thin films with perpendicular magnetic anisotropy can be grown on amorphous planar SiO2 substrate with an underlayer stack of [Pt (3nm)∕Cr (50nm)] adopting a [002] orientation when deposited at 350°C. This knowledge of optimum layer stack was transferred to self-assembled SiO2 particle arrays. While 330nm SiO2 particle arrays reveal perpendicular magnetic anisotropy with a remanence of almost one and a coercivity of 370mT, on 160nm particles, the FePt caps show a (111) texturing, leading to the random orientation of the easy axis of the magnetization.