We illustrate the behaviour of As when it is confined, by the implantation technique, in a SiO{sub 2}(70nm)/Si(30nm)/SiO{sub 2}(70nm) multilayer and its spatial redistribution when annealing processes are performed. By Rutherford backscattering spectrometry and Z-contrast transmission electron microscopy we found an As accumulation at the Si/SiO{sub 2} interfaces and at the Si grain boundaries with no segregation of the As in the Si layer. Such an effect is in agreement with a model that assumes a traps distribution in the Si in the first 2-3 nm above the SiO{sub 2}/Si interfaces and along the Si grain boundaries. The traps concentration at the Si/SiO{sub 2} interfaces was estimated in 10{sup 14} traps/cm{sup 2}. The outlined results can open perspectives on the doping properties of As in Si nanocrystals, whose applications in nanoelectronics and optoelectronics are widely investigated (copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)
Publication date: 
15 Mar 2011

Francesco Ruffino, Maria Miritello, Mario Vincenzo Tomasello, Riccardo De Bastiani, Maria Grazia Grimaldi, CNR-IMM MATIS, Giuseppe Nicotra, Corrado Spinella

Biblio References: 
Volume: 8
Physica Status Solidi C (online)