Van der Waals α-MoO3 samples offer a wide range of attractive catalytic, electronic, and optical properties. We present herein an emission Mössbauer spectroscopy (eMS) study of the electric-field gradient (EFG) anisotropy in crystalline free-standing α-MoO3 samples. Although α-MoO3 is a two-dimensional (2D) material, scanning electron microscopy shows that the crystals are 0.5-5-µm thick. The combination of X-ray diffraction and micro-Raman spectroscopy, performed after sample preparation, provided evidence of the phase purity and crystal quality of the samples. The eMS measurements were conducted following the implantation of 57Mn (t1/2 = 1.5 min), which decays to the 57Fe, 14.4 keV Mössbauer state. The eMS spectra of the samples are dominated by a paramagnetic doublet (D1) with an angular dependence, pointing to the Fe2+ probe ions being in a crystalline environment. It is attributed to an …