This Letter reports on the active dopant profiling and Ohmic contact behavior in degenerate P-implanted silicon carbide (4H-SiC) layers. Hall measurements showed a nearly temperature-independent electron density, corresponding to an electrical activation of about 80% of the total implanted dose. Using the Hall result as calibration, the depth resolved active P-profile was extracted by scanning capacitance microscopy (SCM). Such information on the active P-profile permitted to elucidate the current injection mechanism at the interface of annealed Ni Ohmic contacts with the degenerate n-type 4H-SiC layer. Modeling the temperature dependence of the specific contact resistance with the thermionic field emission mechanism allowed extracting a doping concentration of 8.5 × 1019 cm−3 below the metal/4H-SiC interface, in excellent agreement with the value independently obtained by the SCM depth profiling …